In Situ High-Temperature Structural Analysis of High-Entropy Rare-Earth Sesquioxides

Matheus Pianassola, Kaden Anderson, Can Agca, Chris J. Benmore, Jake W. McMurray, Jöerg C. Neuefeind, Charles Melcher, Mariya Zhuravleva

Chemistry of Materials· Volume 35· Issue 3

Abstract

High-entropy rare-earth (RE) sesquioxides (RE 2 O 3 ) containing five cations in equimolar amounts have been investigated for a variety of applications, but little is known about their polymorphic behavior and coefficient of thermal expansion. Here, we evaluate the effect of the average ionic radius (AIR) on the polymorphism of high-entropy RE 2 O 3 . Powder samples of compositions 1 (Lu,Y,Ho,Nd,La) 2 O 3 (AIR = 0.938 Å) and 2 (Gd,Eu,Sm,Nd,La) 2 O 3 (AIR = 0.982 Å) were synthesized via a wet chemical method, and bead samples were prepared for aerodynamic levitation by melting the powders in a copper hearth. Structural transitions were monitored upon cooling from the melt to 1000 °C via in situ X-ray diffraction on aerodynamically levitated samples. The phase evolution was liquid, hexagonal H-type, and monoclinic B-type for composition 1 and liquid, cubic X-type, H-type, and B-type for composition 2. Based on their AIR, the general polymorphic transformations of the high-entropy RE 2 O 3 follow the trend of single-RE RE 2 O 3, but the transition temperatures differ from those of single-RE RE 2 O 3 . The coefficient of thermal expansion values of the B-type phase of compositions 1 and 2 are similar to those of Gd 2 O 3 and previously published high-entropy RE 2 O 3 .
Source: openalex_inverted_index · Quality: baseline

Research context

OpenAlex topics: High Entropy Alloys Studies · High-Temperature Coating Behaviors · Intermetallics and Advanced Alloy Properties

SciVX discovery tags are terminology-based. OpenAlex topics are source-provided classifications.

Affiliations

Scintillation Materials Research Center, University of Tennessee, Knoxville, Tennessee37996, United States

Department of Materials Science and Engineering, University of Tennessee, Knoxville, Tennessee37996, United States

Materials Science and Technology Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee37831, United States

X-Ray Science Division, Advanced Photon Source, Argonne National Laboratory, Argonne, Illinois60439, United States

Neutron Scattering Division, Oak Ridge National Laboratory, Oak Ridge, Tennessee37831, United States

Department of Nuclear Engineering, University of Tennessee Knoxville, Knoxville, Tennessee37996, United States

Funding

U.S. Department of Homeland Security · Division of Materials Research

References (48)

Show source-provided references
1. Adachi G. · 200410.1007/1-4020-2569-6 ↗
2. 10.1021/acsaelm.1c0068210.1021/acsaelm.1c00682 ↗
3. 10.1016/J.APMT.2021.10110410.1016/J.APMT.2021.101104 ↗
4. 10.1021/acsaelm.1c0070310.1021/acsaelm.1c00703 ↗
5. 10.1016/J.JNUCMAT.2017.08.03110.1016/J.JNUCMAT.2017.08.031 ↗
6. 10.1103/PHYSREVB.92.174101/FIGURES/12/MEDIUM10.1103/PHYSREVB.92.174101/FIGURES/12/MEDIUM ↗
7. 10.1016/J.CALPHAD.2017.07.00110.1016/J.CALPHAD.2017.07.001 ↗
8. 10.1021/cr940055h10.1021/cr940055h ↗
9. 10.1016/S0925-3467(98)00008-110.1016/S0925-3467(98)00008-1 ↗
10. 10.1006/JSSC.2000.907110.1006/JSSC.2000.9071 ↗
11. 10.1038/ncomms948510.1038/ncomms9485 ↗
12. 10.1063/5.000314910.1063/5.0003149 ↗
13. 10.1080/21663831.2016.122043310.1080/21663831.2016.1220433 ↗
14. 10.1111/jace.1697110.1111/jace.16971 ↗
15. 10.1038/s42004-019-0216-210.1038/s42004-019-0216-2 ↗
16. 10.1111/jace.1668910.1111/jace.16689 ↗
17. 10.3390/MA1314314110.3390/MA13143141 ↗
18. 10.1016/J.JALLCOM.2021.16210810.1016/J.JALLCOM.2021.162108 ↗
19. 10.1016/J.JMST.2021.06.05710.1016/J.JMST.2021.06.057 ↗
20. 10.1016/j.jeurceramsoc.2021.01.02710.1016/j.jeurceramsoc.2021.01.027 ↗
21. 10.1002/adsu.20220006710.1002/adsu.202200067 ↗
22. 10.1016/J.JEURCERAMSOC.2020.07.01410.1016/J.JEURCERAMSOC.2020.07.014 ↗
23. 10.1088/1757-899X/1014/1/01205910.1088/1757-899X/1014/1/012059 ↗
24. 10.1007/S40145-021-0461-610.1007/S40145-021-0461-6 ↗
25. 10.1007/BF0055088410.1007/BF00550884 ↗
26. 10.1107/s056774086900322010.1107/s0567740869003220 ↗
27. 10.1107/S002188981300353110.1107/S0021889813003531 ↗
28. 10.1080/23746149.2017.135749810.1080/23746149.2017.1357498 ↗
29. 10.1111/J.1151-2916.1991.TB06947.X10.1111/J.1151-2916.1991.TB06947.X ↗
30. 10.7566/JPSJ.91.09100810.7566/JPSJ.91.091008 ↗
31. 10.1016/J.NIMA.2010.09.12510.1016/J.NIMA.2010.09.125 ↗
32. 10.1063/1.495521010.1063/1.4955210 ↗
33. 10.1107/S160057671600045510.1107/S1600576716000455 ↗
34. 10.1111/J.1151-2916.1972.TB11329.X10.1111/J.1151-2916.1972.TB11329.X ↗
35. Foex M. · Rev. Int. Hautes Temp. Refract. · 1966 · 3 · 429
36. Tresvyatkii S. G. · Colloq. Int. Cent. Nat. Rech. Sci. · 1971 · 205 · 247
37. 10.1016/0022-4596(76)90218-810.1016/0022-4596(76)90218-8 ↗
38. 10.2109/jcersj1950.85.978_9010.2109/jcersj1950.85.978_90 ↗
39. 10.1016/0040-6031(85)85135-210.1016/0040-6031(85)85135-2 ↗
40. 10.1016/J.PMATSCI.2006.09.00210.1016/J.PMATSCI.2006.09.002 ↗
41. 10.1007/s40145-022-0625-z10.1007/s40145-022-0625-z ↗
42. 10.1524/ract.1965.4.4.19710.1524/ract.1965.4.4.197 ↗
43. 10.1021/ACS.INORGCHEM.9B0372610.1021/ACS.INORGCHEM.9B03726 ↗
44. 10.1103/PhysRevB.93.01443710.1103/PhysRevB.93.014437 ↗
45. 10.1016/J.JEURCERAMSOC.2020.10.03910.1016/J.JEURCERAMSOC.2020.10.039 ↗
46. 10.1143/JPSJ.81.02471910.1143/JPSJ.81.024719 ↗
47. 10.1007/bf0239791710.1007/bf02397917 ↗
48. 10.1016/j.jcrysgro.2006.04.04010.1016/j.jcrysgro.2006.04.040 ↗